Montmorillonite

Empirically derived parameters and analytical solutions were used to determine possible mechanistic processes of organo-macromolecular fate in dead-end hyperfiltration at abnormal hydraulic pressure settings. Ideally the concentration polarization is assumed to have an ideal geometry but this may no

In this paper, montmorillonite–Cu(II)/Fe(III) oxides magnetic material was prepared and used for removal of harmful algae from water. The material was prepared by the supporting of Cu(II)/Fe(III) oxides on pillared montmorillonite and was characterized by XRD, zeta potential measurements. The result

Di-p-anisyltelluritrichloride-MM (CH3OPhTeCl3-MM), bi-phenyltelluride-MM (Ph2Te-MM) octadecytrimethylammonium-MM (ODTMA-MM), tetrabutylammonium-MM (TBA-clay), and cetylpyridium-MM (CP-MM) were prepared and characterized to be used for further investigations as adsorbents of organic contaminants incl

Water transport through nanocomposite-based polyamide 12/montmorillonite was investigated by permeation kinetics. Intercalated and semi-exfoliated nanocomposite structures were studied. For low montmorillonite content (£ 5%) a decrease of water permeability was obtained for a both structures and mai